Aluminum 5052-H19 Foil
Subcategory: 5000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal
Close Analogs:
Composition Notes:
Aluminum content reported is calculated as remainder.
Composition information provided by the Aluminum Association and is not for design.
Key Words: UNS A95052; ISO AlMg2.5; Aluminium 5052-H19 Foil; AA5052-H19 Foil
|
|
|
|||||||||||||||||||||||||||||||||||||||||||||
Material Notes:
Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN.
Physical Properties
| Physical Properties | Metric | English | Comments |
| Density | 2.68 g/cc | 0.0968 lb/in³ | AA; Typical |
Mechanical Properties
| Hardness, Brinell | 88 | 88 | 500 kg load with 10 mm ball. Calculated value. |
| Hardness, Knoop | 111 | 111 | |
| Hardness, Rockwell A | 37 | 37 | Converted from Brinell Hardness Value |
| Hardness, Rockwell B | 54 | 54 | Converted from Brinell Hardness Value |
| Hardness, Vickers | 99 | 99 | Converted from Brinell Hardness Value |
| Tensile Strength, Ultimate | 330 MPa | 47900 psi | |
| Tensile Strength, Yield | 325 MPa | 47100 psi | |
| Elongation at Break | 4 % | 4 % | Foil |
| Modulus of Elasticity | 70 GPa | 10200 ksi | Average of Tension and Compression. In Aluminum alloys, the compressive modulus is typically 2% greater than the tensile modulus |
| Poisson’s Ratio | 0.33 | 0.33 | |
| Shear Modulus | 25.9 GPa | 3760 ksi | |
| Shear Strength | 200 MPa | 29000 psi | Calculated value. |
Electrical Properties
| Electrical Resistivity | 4.99e-006 ohm-cm | 4.99e-006 ohm-cm | AA; Typical at 68°F |
Thermal Properties
| CTE, linear 68°F | 23.8 µm/m-°C | 13.2 µin/in-°F | AA; Typical; Average over 68-212°F range. |
| CTE, linear 250°C | 25.7 µm/m-°C | 14.3 µin/in-°F | Average over the range 20-300ºC |
| Specific Heat Capacity | 0.88 J/g-°C | 0.21 BTU/lb-°F | Estimated from trends in similar Al alloys. |
| Thermal Conductivity | 138 W/m-K | 960 BTU-in/hr-ft²-°F | AA; Typical at 77°F |
| Melting Point | 607 – 649 °C | 1125 – 1200 °F | AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater |
| Solidus | 607 °C | 1125 °F | AA; Typical |
| Liquidus | 649 °C | 1200 °F | AA; Typical |
Processing Properties
| Annealing Temperature | 343 °C | 650 °F | holding at temperature not required |
| Hot-Working Temperature | 260 – 510 °C | 500 – 950 °F |