Aluminum 5083-H34; 5083-H343
Subcategory: 5000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal
Close Analogs:
Composition Notes:
Aluminum content reported is calculated as remainder.
Composition information provided by the Aluminum Association and is not for design.
Key Words: UNS A95083; ISO AlMg4.5Mn; Aluminium 5083-H34 and Aluminium 5083-H343; AA5083-H34
|
|
|
||||||||||||||||||||||||||||||||||||||||||||||||
Material Notes:
Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN.
Physical Properties
| Physical Properties | Metric | English | Comments |
| Density | 2.66 g/cc | 0.0961 lb/in³ | AA; Typical |
Mechanical Properties
| Hardness, Brinell | 93 | 93 | 500 kg load with 10 mm ball. Calculated value. |
| Hardness, Knoop | 117 | 117 | Converted from Brinell Hardness Value |
| Hardness, Rockwell A | 39.1 | 39.1 | Converted from Brinell Hardness Value |
| Hardness, Rockwell B | 58 | 58 | Converted from Brinell Hardness Value |
| Hardness, Vickers | 104 | 104 | Converted from Brinell Hardness Value |
| Tensile Strength, Ultimate | 345 MPa | 50000 psi | |
| Tensile Strength, Yield | 280 MPa | 40600 psi | |
| Elongation at Break | 9 % | 9 % | In 5 cm; Sample 1.6 mm thick |
| Modulus of Elasticity | 70.3 GPa | 10200 ksi | In Tension |
| Compressive Modulus | 71.7 GPa | 10400 ksi | |
| Poisson’s Ratio | 0.33 | 0.33 | Estimated from trends in similar Al alloys. |
| Shear Modulus | 26.4 GPa | 3830 ksi | |
| Shear Strength | 210 MPa | 30500 psi |
Electrical Properties
| Electrical Resistivity | 5.9e-006 ohm-cm | 5.9e-006 ohm-cm |
Thermal Properties
| CTE, linear 68°F | 23.8 µm/m-°C | 13.2 µin/in-°F | AA; Typical; Average over 68-212°F range. |
| CTE, linear 250°C | 26 µm/m-°C | 14.4 µin/in-°F | Average over the range 20-300ºC |
| Specific Heat Capacity | 0.9 J/g-°C | 0.215 BTU/lb-°F | |
| Thermal Conductivity | 117 W/m-K | 812 BTU-in/hr-ft²-°F | |
| Melting Point | 591 – 638 °C | 1095 – 1180 °F | AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater |
| Solidus | 591 °C | 1095 °F | AA; Typical |
| Liquidus | 638 °C | 1180 °F | AA; Typical |
Processing Properties
| Annealing Temperature | 413 °C | 775 °F | holding at temperature not required |
| Hot-Working Temperature | 316-482 °C | 600 – 900 °F |